| 牌號(hào) | X19CrMoNbVN11-1 |
|---|---|
| 1.4913 | |
| 對(duì)應(yīng)標(biāo)準(zhǔn) | NF EN 10269-1999
用于高溫或低溫條件下的緊固件用鋼及鎳合金 |
| 歸類 | 合金鋼 |
| 標(biāo)簽 | 淬火回火鋼 |
| 密度 | 7.7 g/cm3 |
-
交付條件下在高溫下的最小屈服強(qiáng)度
Material designation Heat treatment
conditionDiameter
d
mmMinimum 0.2%-proof strength Rp0.2 in MPa at a temperature (in°C) of: Name Number 50 100 150 200 250 300 350 400 450 500 550 600 650 X19CrMoNbVN11-1 1.4913 +QT d≤160 726 701 676 651 643 627 610 577 544 495 412 305 -
-
符合本歐洲標(biāo)準(zhǔn)的產(chǎn)品熱處理指南
Material designation Heat treatment
conditionNormalizing,quenching
or solution annealing
temperature
°CType of
cooling①Tempering or
precipitation
treatment (and time)
°CName Number X19CrMoNbVN11-1 1.4913 +QT 1100 to 1130 a,o 670 to 720（min.2 h） ◎ 根據(jù)原件相關(guān)規(guī)定，如果允許矯直后消除應(yīng)力，應(yīng)選擇消除應(yīng)力的溫度，以獲得規(guī)定的性能。 ① a=air; o=oil; w=water
-
物理性能
各溫度°C時(shí)靜態(tài)彈性模量 20 100 200 300 400 500 600 700 800 GPa 216 209 200 190 179 167 127 - -
-
蠕變性能
Designation Temperature Strength for
1% (plastic)
creep strain ①Creep rupture
strength for ②Name Number °C 10000h 100000h 10000h 100000h 200000h X19CrMoNbVN11-1 1.4913 450 500 448 559 500 486 460 475 416 529 472 450 470 450 388 500 444 425 480 424 358 473 414 395 490 398 328 446 383 364 500 374 298 417 349 330 510 349 268 392 314 291 520 323 238 366 276 253 530 298 210 340 237 209 540 274 181 314 201 172 550 250 153 288 161 130 560 225 - 259 132 102 570 201 - 234 105 81 580 177 - 208 86 66 590 154 - 181 72 52 600 133 - 155 65 49 ◎ The values given in this table are the mean values of the scatter band so far obtained, which will be checked from time to time as further test results become available and if necessary corrected.
◎ * and () indicate values of extended stress extrapolation or time extrapolation, respectively.
① This is the stress relative to the initial cross- section leadina to a permanent elongation of 1 % after 10000 h and 100000 h.
② This is the stress relative to the initial cross- section leading to fracture after 10000 h, 100000 h and 200000 h.
-
松弛性能
Material designation Temperature
℃for an
initial strain
∈A total
%Residual stress in N/mm2
after stressing duration forName Number 1000
h10000
h30000
hX19CrMoNbVN11-1 1.4913 400 0.2 262 237 206 410 257 231 202 420 252 225 199 430 246 218 195 440 240 212 190 450 234 206 185 460 228 198 180 470 221 191 173 480 214 183 165 490 207 175 157 500 199 166 147 510 190 155 136 520 181 143 124 530 171 130 108 540 160 114 92 550 149 98 79 560 134 78 66 570 118 63 53 580 100 48 40 590 80 39 30 600 61 30 21 ◎ The values given in this table are the mean values of the scatter band so far obtained, which will be checked from time to time as further test results become available and if necessary corrected.